Hochreines Pseudoböhmit | Katalysatorbinder

Hohe Reinheit

Produktübersicht

Angebot anfordern Muster anfordern

200-400

Spezifische Oberfläche (m²/g)

0.5-1.2

Porenvolumen (cm³/g)

≥65%

Al₂O₃-Gehalt

≤0.05%

Na₂O-Gehalt

BET-Oberfläche	200-400 m²/g	Porenvolumen	0,8-1,5 cm³/g
Porengröße	3-15 nm	pH	7-9

Product	Grade	CaO (%)	SiO₂ (%)	Fe₂O₃ (%)	Na₂O (%)	Surface area (m²/g)	Pore volume (ml/g)	Dry basis (%)	Peptization (%)
Silica-free high-pore	CP-1	≤0.02	≤0.02	≤0.01	≤0.05	280–300	≥1.2	70±2	20–30
Silica-free high-pore	CP-2	≤0.02	≤0.02	≤0.01	≤0.05	≥300	≥1.1	70±2	5–20
Silica-free high-pore	CP-3	≤0.02	≤0.02	≤0.01	≤0.05	≥300	≥1.1	70±2	20–30
High-silica high-pore	CP-4	≤0.02	≤0.02	≤0.01	≤0.05	≥300	≥1.1	70±2	30–40
High-silica high-pore	CP-S-1	≤0.02	0–2	≤0.01	≤0.05	≥360	≥1.2	70±2	–
High-silica high-pore	CP-S-2	≤0.02	2–4	≤0.01	≤0.05	≥380	≥1.2	70±2	–

Product	Grade	CaO (ppm)	SiO₂ (ppm)	Fe₂O₃ (ppm)	Na₂O (ppm)	Surface area (m²/g)	Pore volume (ml/g)	Dry basis (%)	Peptization (%)
High-purity high-pore	HP-1	≤50	≤50	≤50	≤50	≥300	≥1.1	70±2	20–30
High-purity high-pore	HP-2	≤50	≤50	≤50	≤50	≥300	≥1.1	70±2	30–40
High-purity high-pore	HP-3	≤50	≤50	≤50	≤50	≥300	≥1.1	70±2	40–55
High-silica high-purity	HP-S-1	≤50	0–2%	≤50	≤50	≥360	≥1.1	70±2	–
High-silica high-purity	HP-S-2	≤50	2–4%	≤50	≤50	≥380	≥1.2	70±2	–

Note: Specifications can be adjusted to customer requirements.

Pseudoböhmit wird in vielen Branchen mit hervorragender Leistung eingesetzt.

⚗️

Vorstufe für γ-Aluminiumoxid-Träger, weit verbreitet in Raffination und Petrochemie.

💧

Hohe spezifische Oberfläche ideal für Gas- und Flüssigkeitsreinigung.

🏗️

Herstellung leistungsfähiger Keramik und Feuerfeststoffe.

🔬

Wichtiges Rohmaterial und Zwischenprodukt in der Feinchemie.

Kontaktieren Sie unser Vertriebsteam für Angebote, Lieferzeiten und kundenspezifische Spezifikationen.

Vertrieb kontaktieren Muster anfordern